PERMA FILM System

PERMA FILM is a 1-component surface-tolerant thick film paint. This calcium sulfonate compound dissolved in resin provides effective rust protection for all bare, rusted or old-coated ferrous metals.

FIELDS OF APPLICATION

Ballast water tanks, damp empty cells, offshore and industrial plants, machine parts, tools and equipment during sea transport and longer external storage, wheelhouses, underbody, winter service and equipment.

WORKING METHOD – PERMA FILM SYSTEM

Surface preparation: high-pressure washing and removal of loose components with the wire brush. The surfaces can be wet, but without water drops. Apply as Pre-Primer FLUID FILM Liquid A/NAS or AS-R by nebulization (layer thickness max. 10-15μm). PERMA FILM is ready for use and can then be processed directly with the pressure cup gun after the ACTION of the FLUID FILM. By combining it with FLUID FILM, the system remains flexible in itself, hardens on the surface and combines the positive properties such as the penetrability of FLUID FILM with those of a grip-resistant protective layer.

A prerequisite for reliable corrosion protection and good adhesion is a dry layer thickness of at least 150μm. This layer thickness is obtained after 2-3 applications when applied with a brush or roller, and after 1 application when spraying (wet layer thickness 250μm).

For the maintenance of ballast water tanks, we recommend preparing the surface according to the degree of cleaning ST2 or Wa2 by high-pressure washing and spraying FLUID FILM Liquid A as an active rust primer. PERMA FILM should then be applied in 2 layers. The first in a wet layer thickness of 150μm (dry layer thickness 100μm) and the second in a wet layer thickness of 250μm (dry layer thickness 150μm).

For further information, please refer to our technical data sheets.

PROPERTIES / EFFECT

• Rust protection and top coating in one
• resistant to splashing water and stone chipping
• the platelet-shaped structure of the film-forming components forms a physical barrier, provides mechanical strength and prevents the penetration of water and oxygen to the base metal
• can be repaired selectively in the event of mechanical injuries
• saltwater resistant
• Processing also possible at low temperatures (from + 5 °C)
• dust-dry after 12 hours (ambient temperature 20-25 °C)

Container sizes

• 1 ltr. tin
• 3 ltr. bucket
• 20 ltr. bucket